Abstract In this study, we aimed to evaluate the halitosis and pain threshold of the peri-implant soft tissues in individuals rehabilitated with implant-supported prostheses. Forty-eight subjects were divided into four groups (n = 12) according to their prosthetic rehabilitation: single-tooth fixed prosthesis, multi-tooth fixed prosthesis, overdentures, and the Brånemark protocol. Halitosis was measured using a halimeter, whereas the pain threshold was measured using Von Frey monofilaments. Measurements were taken before (t0) and 30 days after (t1) placement of healing caps, and at the time of (t2) and 30 days after (t3) prosthetic placement. Halitosis data were analyzed using the chi-square test and Bonferroni correction (p < 0.05). Two-way ANOVA and Tukey’s test (p < 0.05) were used to analyze pain threshold data. We noted an association between halitosis and time for the Brånemark protocol [X2(6) = 18.471; p = 0.005] and overdenture groups [X2(6) = 17.732; p = 0.007], and between halitosis and type of prosthesis only at t0 [X2(6) = 12.894; p = 0.045]. The interaction between time and the type of prosthesis significantly interfered with the mean pain threshold values (p = 0.001). At most time points, the majority of participants in each group had clinically unacceptable halitosis. After 30 days of using the prostheses, the overdenture group had a lower pain threshold compared to the Brånemark protocol group.

Resumo Este estudo teve como objetivo avaliar a halitose e o limiar de dor dos tecidos moles peri-implantares em indivíduos reabilitados com próteses implantossuportadas. Um total de 48 indivíduos foram divididos em quatro grupos (n=12), de acordo com as reabilitações: prótese fixa unitária, prótese fixa multidentária, sobredentadura e protocolo de Brånemark. A halitose foi medida com um halímetro, enquanto o limiar de dor foi medido com monofilamentos de von Frey. As medições foram feitas antes (t0) e 30 dias após (t1) a colocação das tampas de cicatrização e no momento (t2) e 30 dias após (t3) a colocação da prótese. Os dados de halitose foram analisados por meio do teste qui-quadrado e correção de Bonferroni (p < 0,05). ANOVA de duas vias e o teste de Tukey (p < 0,05) foram usados para analisar os dados do limiar de dor. Observou-se associação entre halitose e tempo para o protocolo de Brånemark [X2(6) = 18,471; p = 0,005] e grupos overdenture [X2(6) = 17,732; p = 0,007], e entre halitose e tipo de prótese apenas em t0 [X2(6) = 12,894; p = 0,045]. A interação entre o tempo e o tipo de prótese interferiu significativamente nos valores médios do limiar de dor (p = 0,001). Na maioria dos pontos de tempos, a maioria dos participantes de cada grupo apresentava halitose clinicamente inaceitável. Após 30 dias de uso das próteses, o grupo overdenture apresentou menor limiar de dor em comparação ao grupo do protocolo de Brånemark.

RESUMO Objetivo: O presente estudo teve como objetivo avaliar a estabilidade dimensional e manutenção de detalhes de alginatos convencionais e de alta estabilidade por até 5 dias de armazenamento. Métodos: Para esse estudo, foram selecionados dois tipos de alginatos: convencional (Hydrogum) (n = 10) e de alta estabilidade (Hydrogum 5) (n = 10), sendo produzidos com o auxílio de um bloco metálico cilíndrico e um molde metálico em forma de anel (especificações 18, 19 e 25, ANSI/ADA). Para o teste de estabilidade dimensional, dez imagens foram obtidas imediatamente e para cada tempo de armazenamento (15 min, 24, 48, 72, 96 e 120 horas), realizadas por câmera digital. As amostras foram mantidas hermeticamente fechadas em sacos plásticos (23°C). Para o teste de reprodução de detalhes, as amostras foram utilizadas para obter 140 (n = 70 por grupo) modelos de gesso, sendo observada a precisão angular de três sulcos (20 µm, 50 µm e 75 µm) para cada período. A precisão da reprodução de detalhes foi classificada usando uma classificação de pontuação predeterminada. As medições das mudanças dimensionais foram feitas no programa Corel DRAW X6. Os dados foram submetidos ao teste t de Student (α = 0,05). Resultados: Foi observada diferença estatística em relação à matriz após 24h para ambos os alginatos. Uma mudança dimensional linear negativa estatisticamente significativa (contração) foi verificada após 24 h de armazenamento (1,52% para alginato de alta estabilidade; 1,32% para alginato convencional). O alginato de alta estabilidade manteve os detalhes completos por até 72 horas, enquanto o alginato convencional, por 24 horas. Os alginatos reproduziram o sulco de 75 µm para todos os períodos. Conclusão: As impressões feitas com ambos os alginatos devem ser imediatamente vazadas para se ter resultados clínicos satisfatórios.

ABSTRACT Objective: This study aimed to evaluate the dimensional stability and maintenance of details of conventional and high stability alginates up to 5-day storage. Methods: Two types of alginates were selected (n=10) for this study, conventional (Hydrogum) and high stability alginates (Hydrogum 5), which were produced with the aid of a cylindrical metal block and a ring-shaped metal mold (Specifications 18, 19, and 25, ANSI/ADA). Ten images were obtained from the molds for the dimensional stability test, which were taken immediately after their production and at each different storage periods (15 min, 24 h, 48 h, 72 h, 96 h, and 120 h) by a digital camera. The specimens were kept hermetically sealed in plastic bags (23°C) and then used to obtain 140 (n=70) dental stone models, used in the detail reproduction test, in which the angular accuracy of three grooves (20 µm, 50 µm, and 75 µm) was observed at each period. The details reproduction accuracy was classified using a predetermined score classification. Measurements of dimensional changes were made in the Corel DRAW X6 program. The data were submitted to the Student’s t-test (α?#8197;= 0.05). Results: A statistically significant difference concerning the size of the matrix was observed after 24h for both alginates, and a statistically significant negative linear dimensional change (contraction) was verified after 24 h of storage (1.52% for the high stability alginate, and 1.32% for the conventional alginate). The high stability alginate kept the full details for 72 hours, while the conventional alginate, for 24 h. Both alginates reproduced the 75 µm groove at all storage periods. Conclusion: Impressions made with both alginates presented satisfactory clinical results when the alginates were immediately poured.

OBJECTIVE: The aims of this study were to examine the trans- and postoperative systemic characteristics of patients undergoing dental implant surgery and to investigate the relationship between pre- and post- surgery anxiety levels. MATERIAL AND METHODS: Thirty-nine patients were analyzed in 3 call centers to determine anxiety levels, pain levels, and preoperative and postoperative histories using the State-Trait (STAI) questionnaire. RESULTS: A total of 93 dental implants were installed, with a success rate of 100%. The most frequently reported systemic disease was hypertension. There was a significantly higher rate of effective clamping (torque) to the mandibular bone than to the maxillary bone. The association between postoperative surgical complications and longer operative time was not significant, but there was a significant correlation between the alteration of mouth opening and daily routine activities and a significant decrease in anxiety levels between the day of surgery and the postoperative time point (p =0.006). CONCLUSION: A longer surgical time was associated with surgery-related complications and with a higher anxiety index on the preoperative evaluation.

Purpose: The aim of this study was to evaluate the effect of a surface treatment with Sofreliner primer on tensile bond strength of a resin-based soft liner (Coe-Soft) bonded to a polymethylmethacrylate (PMMA) resin before and after accelerated aging simulated by a thermocycling machine. Material and Methods: One hundred and twenty rectangular specimens of PMMA resin were fabricated with 10 × 10 mm² of cross-section and 40 mm of height. The resin-based soft liner was positioned between two PMMA resin specimens. The specimens were divided randomly into 6 groups (n = 10) according to the surface treatment and accelerated aging cycles (0, 500 and 1000). After accelerated aging, specimens were submitted to tensile bond strength test. The fractures were classified as adhesive, cohesive or both. Results: Most failures were classified as cohesive (p = 0.025) and there was an increase on the mean values of tensile bond strength for group with primer application regardless the cycles of accelerated aging, and also an increase along thermocycling periods. The scanning electronic microscopy was used to illustrate the types of failures and the effect of primer application on PMMA acrylic resin surface. Conclusion: The primer application associated with resin-based soft liners is clinically viable, once this treatment strategy provides a reliable adhesion.

The aim of this study was to evaluate the effect of thermocycling and immersion in mouthwash or beverage solutions on the color stability of four different acrylic resin-based dentures (Onda Cryl, OC; QC20, QC; Classico, CL; and Lucitone, LU). The factors evaluated were type of acrylic resin, immersion time, and solution (mouthwash or beverage). A total of 224 denture samples were fabricated. For each type of resin, eight samples were immersed in mouthwashes (Plax-Colgate, PC; Listerine, LI; and Oral-B, OB), beverages (coffee, CP; cola, C; and wine, W), and artificial saliva (AS; control). The color change (DE) was evaluated before (baseline) and after thermocycling (T1), and after immersion in solution for 1 h (T2), 3 h (T3), 24 h (T4), 48 h (T5), and 96 h (T6). The CIE Lab system was used to determine the color changes. The thermocycling test was performed for 5000 cycles. Data were submitted to three-way repeated-measures analysis of variance and Tukey's test (p < 0.05). When the samples were immersed in each mouthwash, all assessed factors, associated or not, significantly influenced the color change values, except there was no association between the mouthwash and acrylic resin. Similarly, when the samples were immersed in each beverage, all studied factors influenced the color change values. In general, regardless of the solution, LU exhibited the greatest DE values in the period from T1 to T5; and QC presented the greatest DE values at T6. Thus, thermocycling and immersion in the various solutions influenced the color stability of acrylic resins and QC showed the greatest color alteration.

The development of implant dentistry improved the possibilities of rehabilitation with maxillofacial prosthesis. However, clinically it is difficult to bond the silicone to the attachment system. OBJECTIVES: This study aimed to evaluate the effect of an adhesive system on the bond strength between acrylic resin and facial silicone. MATERIAL AND METHODS: A total of 120 samples were fabricated with auto-polymerized acrylic resin and MDX 4-4210 facial silicone. Both materials were bonded through mechanical retentions and/or application of primers (DC 1205 primer and Sofreliner primer S) and adhesive (Silastic Medical Adhesive Type A) or not (control group). Samples were divided into 12 groups according to the method used to attach the silicone to the acrylic resin. All samples were subjected to a T-peel test in a universal testing machine. Failures were classified as adhesive, cohesive or mixed. The data were evaluated by the analysis of variance (ANOVA) and the Tukey's HSD test (α=.05). RESULTS: The highest bond strength values (5.95 N/mm; 3.07 N/mm; 4.75 N/mm) were recorded for the samples that received a Sofreliner primer application. These values were significantly higher when the samples had no scratches and did not receive the application of Silastic Medical Adhesive Type A. CONCLUSIONS: The most common type of failure was adhesive. The use of Sofreliner primer increased the bond strength between the auto-polymerized acrylic resin and the Silastic MDX 4-4210 facial silicone.

The use of ocular prostheses for ophthalmic patients aims to rebuild facial aesthetics and provide an artificial substitute to the visual organ. Natural intemperate conditions promote discoloration of artificial irides and many studies have attempted to produce irides with greater chromatic paint durability using different paint materials. OBJECTIVES: The present study evaluated the color stability of artificial irides obtained with two techniques (oil painting and digital image) and submitted to microwave polymerization. MATERIAL AND METHODS: Forty samples were fabricated simulating ocular prostheses. each sample was constituted by one disc of acrylic resin N1 and one disc of colorless acrylic resin with the iris interposed between the discs. The irides in brown and blue color were obtained by oil painting or digital image. The color stability was determined by a reflection spectrophotometer and measurements were taken before and after microwave polymerization. Statistical analysis of the techniques for reproducing artificial irides was performed by applying the normal data distribution test followed by 2-way ANOVA and Tukey HSD test (α=.05). RESULTS: Chromatic alterations occurred in all specimens and statistically significant differences were observed between the oil-painted samples and those obtained by digital imaging. There was no statistical difference between the brown and blue colors. Independently of technique, all samples suffered color alterations after microwave polymerization. CONCLUSION: The digital imaging technique for reproducing irides presented better color stability after microwave polymerization.

Esthetics and durability of materials used to fabricate artificial eyes has been an important issue since artificial eyes are essential to restore esthetics and function, protect the remaining tissues and help with patients' psychological therapy. However, these materials are submitted to degrading effects of environmental agents on the physical properties of the acrylic resin. OBJECTIVE: This study assessed the color stability of acrylic resins used to fabricate sclera in three basic shades (N1, N2 and N3) when subjected to accelerated aging, mechanical and chemical polishing. MATERIAL AND METHODS: Specimens of each resin were fabricated and submitted to mechanical and chemical polishing. Chromatic analysis was performed before and after accelerated aging through ultraviolet reflection spectrophotometry. RESULTS: All specimens revealed color alteration following polishing and accelerated aging. The resins presented statistically significant chromatic alteration (p<0.01) between the periods of 252 and 1008 h. CONCLUSIONS: Both polishing methods presented no significant difference between the values of color derivatives of resins.

We evaluated the effects of disinfection and aging on the hardness of silicones containing opacifiers and intended for use in facial prosthetics. A total of 90 samples were produced using a cylindrical metal mold 3 mm in height and 30 mm in diameter. The samples were fabricated from Silastic MDX 4-4210 silicone in three groups: GI contained no opacifier, GII contained barium sulfate (Ba), and GIII contained titanium dioxide (Ti). The samples were disinfected using effervescent tablets (Ef), neutral soap (Ns), or 4% chlorhexidine (Cl) 3 times a week for 60 days. After this period the samples underwent 1,008 hours of accelerated aging. The hardness was measured using a durometer immediately following the disinfection period and after 252, 504, and 1,008 hours of aging. The data were statistically analyzed using 3-way ANOVA and the Tukey test (p < .05). The GIII group exhibited the greatest variation in hardness regardless of elapsed time. All groups displayed greater hardness after 1,008 hours of accelerated aging independent of disinfectant type. All of the hardness values were within the clinically acceptable range.

Acrylic resins have been widely used due to their acceptable esthetics and desirable characteristics such as easy handling, good thermal conductivity, low permeability to oral fluids and color stability. Flexible resins were introduced on the market as an alternative to the use of conventional acrylic resins in the construction of complete and partial removable dentures. Although these resins present advantages in terms of esthetics and comfort, studies assessing chromatic and microhardness alterations of these materials are still scarce in the related literature. The aim of this study was to evaluate the chromatic and microhardness alterations of two commercial brands of flexible resins in comparison to the conventional resin Triplex when submitted to accelerated aging. The resins were manipulated according to manufacturers' instructions and inserted into a silicone matrix to obtain 21 specimens divided into 3 groups: Triplex, Ppflex and Valplast. Triplex presented the highest microhardness value (p < 0.05) for all the aging periods, which was significantly different from that of the other resins, followed by the values of Valplast and Ppflex. Comparison between the flexible resins (Ppflex and Valplast) revealed a statistically significant difference (p < 0.05) as regards color. The flexible resin Ppflex and the conventional resin Triplex presented no statistically significant difference (p < 0.05) as regards aging. The accelerated aging significantly increased the microhardness values of the resins, with the highest values being observed for Triplex. Valplast presented the greatest chromatic alteration after accelerated aging.

The purpose of this study was to assess color alteration of the paints used for iris painting in artificial eyes. Five disks of heat cured acrylic resin were confectioned by microwave energy for each paint analyzed, in a total of 40 specimens. Each specimen consisted of a colorless acrylic resin disk and another of equal size, of scleral white colored acrylic resin, with the painting interposed between the two disks. The specimens were submitted to an accelerated aging process in a chamber under ultraviolet radiation for 1,008 hours. To assess color variation, a reflective spectrophotometer was used. The results were statistically analyzed by ANOVA and the Tukey test (p < 0.05). All the paints underwent chromatic alteration. The oil paint presented the highest resistance to accelerated aging.

Prosthetic eyes are artificial substitutes for the eyeball, made of heat-curing acrylic resin, serving to improve the esthetic appearance of the mutilated patient and his/her inclusion in society. The aim of this study was to assess the flexural strength of two heat-curing acrylic resins used for manufacturing prosthetic eyes. Thirty-six specimens measuring 64 x 10 x 3.3 mm were obtained and divided into four groups: acrylic resin for artificial sclera N1 (Artigos Odontológicos Clássico, São Paulo, SP, Brazil), heat-cure water technique (GI) and microwave-cured (GII); colorless acrylic resin for prosthetic eyes (Artigos Odontológicos Clássico, São Paulo, SP, Brazil), heat-cure water technique (GIII) and microwave-cured (GIV). Mechanical tests using three point loads were performed in a test machine (EMIC, São José dos Pinhais, PR, Brazil). The analysis of variance and the Tukey test were used to identify significant differences (p < 0.01). Groups GII and GIV presented, respectively, the highest (98.70 ± 11.90 MPa) and lowest means (71.07 ± 8.93 MPa), with a statistically significant difference. The cure method used for the prosthetic eye resins did not interfere in their flexural strength. It was concluded that all the resins assessed presented sufficient flexural strength values to be recommended for the manufacture of prosthetic eyes.

One of the greatest challenges faced by buccomaxillofacial prosthetists is to reproduce the patient's exact skin color and provide adequate esthetics. To reach this objective, professionals must use materials with easy characterization and that maintain color over long periods of time. The objective of this study was, thus, to evaluate the color stability of two types of silicones, Silastic 732 and Silastic MDX4-4210. Twenty-four test specimens were made from each type of silicone and were divided into a colorless group and groups intrinsically pigmented with ceramics, cosmetics or iron oxide. The specimens were submitted to an accelerated system of aging for non-metallic materials. Readings were carried out initially and after periods corresponding to 163, 351, 692 and 1,000 hours of aging, using a reflection spectrophotometer analysis, and color alterations were calculated by the CIE L*a*b* system. The data were submitted to variance analysis and Tukey's test at a 5% level of probability. The results demonstrated that, irrespective of the period of time analyzed, all the materials underwent some type of chromatic alteration (ΔE > 0). The test specimens made with Silastic 732 and MDX4-4210, without pigmentation, presented the lowest color alteration values after 1,000 hours of aging. Of the pigments, ceramic presented the lowest color alteration values and cosmetic powder presented the highest values. Thus, it may be concluded that the materials without the incorporation of pigments presented similar color alteration values, and did not differ statistically. The cosmetic powder used in this study was the pigment that most altered the color of the test specimens.

The purpose of this study was to evaluate the Shore A hardness and surface roughness of two silicones for maxillofacial prosthetic treatment, under the influence of chemical disinfection and storage. Twenty-eight specimens were obtained, half of which were made of Silastic MDX 4-4210 silicone and, the other half were made of Silastic 732 RTV silicone. The specimens were divided into four groups: Silastic 732 RTV and MDX 4-4210 with disinfection 3 times a week with Efferdent tablets and the same materials without disinfection. The hardness of the materials was analyzed with a Shore A Durometer. The surface roughness was established by a digital portable roughness tester, initially and 2 months after the confection of the specimens. A variance test was applied (2-way ANOVA), followed by Tukey test (the level of significance was set at 1%). The storage time factor statistically influenced (p < 0.01) the materials' properties of hardness and roughness. MDX 4-4210 (28.59 Shore A, 0.789 Ra) presented higher values than Silastic 732 RTV (18.08 Shore A, 0.656 Ra) for both properties. Regarding the disinfection period, there was no significant difference in any of the materials tested.

O objetivo deste estudo foi avaliar a alteração dimensional de bases de prótese total confeccionadas com diferentes resinas após diferentes períodos de armazenagem. Para isso foram confeccionados 25 conjuntos modelo de gesso/base de resina, utilizando-se quatro resinas acrílicas: QC-20 submetida à polimerização convencional e por energia de microondas, Vip Cril submetida à polimerização convencional, Vip Wave e Onda Cryl submetida à polimerização por energia de microondas. Após a polimerização, as amostras foram seccionadas para realização de leituras de adaptação com auxílio de um microscópio comparador. As leituras foram realizadas em três pontos: crista do rebordo direito (A) e esquerdo (B), e região mediana do palato, em quatro diferentes períodos. Os resultados foram submetidos à análise de variância e ao teste de Tukey com nível de significância de 5%. A pior adaptação foi verificada na região palatina posterior da base (M) com diferença estatisticamente significante (p<0,05) para as resinas estudadas. Todas as bases de resinas apresentaram alteração dimensional e o período de armazenagem foi um fator que influenciou essa alteração.

The aim of this study was to evaluate the dimensional changes of denture bases made from different resins after different storage periods. For this purpose, 25 sets of plaster models/resin bases were prepared using 4 acrylic resins submitted to two types of polymerization: 1- QC-20 submitted to polymerization by microwave energy; 2- QC-20 submitted to polymerization by water hot bath; 3- Vipi Cril submitted to polymerization by water hot bath; 4- Vipi Wave submitted to polymerization by microwave energy; and 5- Onda Cryl submitted to polymerization by microwave energy. After polymerization, the specimens were sectioned for accuracy readings using a comparison microscope. Readings were taken at 3 points: the crests of the right (A) and left (B) ridges, and the median region of the palate, in 4 different periods. The data obtained were submitted to two-way ANOVA and Tukey's test at 5% significance level. The greatest distortions were found in the posterior palatal region of the base (M), with statistically significant difference (p<0.05) for the studied resins. All acrylic resins presented dimensional changes and the storage period influenced these alterations.